Specializing In The Production Of Inconel601/ UNS N06601/ Alloy601 Seamless Pipe, Sheet, Bar
Available Products
Seamless tube, Plate, Rod, Forgings, Fasteners, Pipe Fittings
Production Standards
| Product | ASTM |
| Bar and wire | B 166 |
| Plate, Sheet and Strip | B 168, B 906 |
| Seamless pipe，tube | B 167, B 829 |
| Welded pipe | B 517, B 775 |
| Weld tube | B 516, B 751 |
| Welded pipe fittings | B 366 |
| Billets and billets for forging | B 472 |
| Forging | B 564 |
Chemical Composition
|
% |
Ni |
Cr |
Fe |
C |
Mn |
Si |
S |
Al |
Cu |
|
Min |
58.0 |
21.0 |
balance |
|
|
|
|
1.00 |
|
|
Max |
63.0 |
25.0 |
0.10 |
1.00 |
0.50 |
0.015 |
1.70 |
1.00 |
Physical Properties
| Density | 8.11 g/cm3 |
| Melting | 1360-1411℃ |
Inconel 601 Features
Inconel 601 is both high temperature and corrosion resistant. An important property of Inconel 601 is its excellent resistance to oxidation at temperatures up to 1200°C, as well as high strength, ease of processing and resistance to water corrosion.
Inconel 601 has excellent oxidation resistance at high temperature, very good carbonization resistance, good oxidation resistance in sulfur-containing atmosphere, good mechanical properties at room temperature and high temperature, good stress corrosion cracking resistance due to Controlling the carbon content and grain size, 601 has a higher creep rupture strength, so it is recommended to use 601 in the field above 500 °C.
Inconel 601 Chemical Characteristics
1. Excellent oxidation resistance at high temperature
2. Good carbonization resistance
3. Good oxidation resistance in sulfur-containing atmosphere
4. Good mechanical properties at both room temperature and high temperature
5. Good resistance to stress corrosion cracking. Due to the control of carbon content and grain size, 601 has high creep rupture strength, so 601 is recommended in the field above 500 °C.
Metallographic structure of Inconel 601:
601 is a face-centered cubic lattice structure.
Corrosion resistance of Inconel 601:
An important property of alloy 601 is its resistance to oxidation at temperatures up to 1180°C. Even under severe conditions, such as during heating and cooling cycles, 601 produces a dense oxide film for high spalling resistance. 601 has very good carbonization resistance. Due to its high chromium and aluminum content, 601 has good oxidation resistance in high temperature sulfur-containing atmospheres.
Application
1. Trays, baskets and fixtures for heat treatment factories.
2. Steel wire split annealing and radiant tubes, high-speed gas burners, wire mesh belts in industrial furnaces.
3. Isolation tanks in ammonia reforming and catalytic support grids in nitric acid production.
4. Exhaust system components
5. Combustion chamber of solid waste incinerator
6. Duct Support and Soot Handling Components
7. Exhaust gas detoxification system components
8. Oxygen reheater